EPOXY RESIN ELECTRONIC POTTING COMPOUND 4 THICK POURS HIGH THERMAL CONDUCTIVITY

Description: 9. Pour the mixture into another clean container and mix for another minute. This will ensure a thoroughly mixed resin is achieved and.10. Pour the mixed MAX EPC into the component housing to be encapsulated ensuring complete and level coverage.Dispense only from one corner of the component casing and allow the material to completely flow and fill the casing and encapsulate the circuit.This technique will reduce voids and air entrapment. GENERAL CURING Allow to cure at room temperature between 20°C to 30°C for 24 to 36 hours. MAX EPC may take longer to react at lower cure temperatures. See the table below for accelerated curing schedule. If available, use a Durometer to determine the cured hardness; a reading of 65 D will be sufficient for handling. To check cure attempt to indent the casting with using your fingernail, if it does not indent then it can be handled. Post Curing For Faster Cure Times To accelerate the curing process, allow the the filled enclosure to cure for 8 hours at room temperature. Once the MAX EPC pour has converted to a solid phase, place under a heat lamp or processing oven set at 50°C to 60°C for 4 hours to accelerate the cure time or hardening. PHYSICAL PROPERTIES Viscosity Part A 6,200 cPs at 25 °C Viscosity Part B 143 cPs at 25 °C Mixed Viscosity 3,220 cPs at 25 °C Mix Ratio By Weight 100:25 Parts B (4:1) By Weight Mixed Color Opaque Black Mixed Density 1.60 g/cc Working Time 120 Minutes (500-gram mass) Peak Exotherm 90°C Max (500-gram mass) Cure Schedule 8 Hours Dry To The Touch at 25°C 24 Hours @25°C -90% Cure 96 Hours Full Cure Time At 25°C Accelerated Cure Allow To Cure For 3 Hours @ 25°C Then Post Cure at 120°C for 1 Hour MECHANICAL PROPERTIES Shore Hardness 85 Shore D After 48 Hours @ 25°C Shrinkage Less Than 0.20% Upon Full Cure Compressive Strength 13,800 psi Tensile Strength 9,900 psi Tensile Elongation 4% Maximum Thermal Conductivity 1.7 to 1.85 W/(mK) Maximum Operating Temperature 110°C ELECTRICAL PROPERTIES Volume Resistivity 4.7 X 1013 Ohms-Cm Dielectric Strength-60 Cycles 500 Volts/Mil Dielectric Constant 4.0 (10 kHz) Dissipation Factor .014 (10 kHz PLEASE CHECK OUT OTHER AVAILABLE RESIN SYSTEMS AT OUR eBay STOREFor our complete listing, please Visit our eBay store!**********************************************DON'T FORGET OUR EPOXY MIXING KITClick The Link To Add To Order https://www.ebay.com/itm/222623932456EVERYTHING YOU NEED TO MEASURE, MIX, DISPENSE OR APPLY Proportioning the correct amount is equally as important to attain the intended cured properties of the resin system.The container in which the epoxy and curing agent is mixed is an important consideration when mixing an epoxy resin system.The container must withstand the tenacity of the chemical and must be free of contamination.Most epoxy curing agent has a degree of corrosivity, as a general practice, protective gloves should be worn when handling chemicals of the same nature. MIXING KIT CONTENTS 1 Each Digital Scale -Durable, Accurate Up To 2000.0 Grams 4 Each 32-ounce (1 Quart) Clear HDPE Plastic Mix Cups4 Each 16-ounce (1 Pint) Clear HDPE Plastic Mix CupsOne Size Fits All Powder-Free Latex Gloves 2 Each Graduated SyringesWooden Stir SticksAssorted Size Foam Brush IMPORTANT NOTICEYour purchase constitutes the acceptance of this disclaimer. Please review before purchasing this product.The user should thoroughly test any proposed use of this product and independently conclude the satisfactory performance in the application. Likewise, if the manner in which this product is used requires government approval or clearance, the user must obtain said approval.The information contained herein is based on data believed to be accurate at the time of publication. Data and parameters cited have been obtained through published information, PolymerProducts and Polymer Composites Inc. laboratories using materials under controlled conditions. Data of this type should not be used for a specification for fabrication and design. It is the user's responsibility to determine this Composites fitness for use.There is no warranty of merchantability for fitness of use, nor any other express implied warranty. The user's exclusive remedy and the manufacturer's liability are limited to refund of the purchase price or replacement of the product within the agreed warranty period. PolymerProducts and its direct representative will not be liable for incidental or consequential damages of any kind. Determination of the suitability of any kind of information or product for the use contemplated by the user, the manner of that use and whether there is any infringement of patents is the sole liability of the user.

Price: 57.46 USD

Location: Ontario, California

End Time: 2023-09-02T19:05:39.000Z

Shipping Cost: 0.72 USD